Chuaiphan, Wichan, Srijaroenpramong, Loeshpahn, Pinpradub, Dumrongrit |
| Zdroj: |
Applied Mechanics and Materials; August 2013, Vol. 389 Issue: 1 p237-244, 8p |
| Abstrakt: |
This work studied the effect of tin (1%Sn) addition in brass 60%Cu+40%Zn (commercial grade) by casting process conducted poured melt metals inside a sand mould and heat treatment in cast brass on microstructure and mechanical properties for solving the cracking of nut and bolt. Three conditions of brass sample for experiment viz.- brass 60%Cu + 40%Zn (commercial grade), brass 60%Cu + 39%Zn+1%Sn (as-cast) and brass 60%Cu+39% Zn+1%Sn (precipitation hardening). The microstructure of specimens all condition, it was found that consists of α phase and β phase. Which brass addition 1% Sn, the β phase content in α phase matrix structure more than brass commercial grade. For microstructure of brass produce by precipitation hardening, shape of α phase are slender and long which have slight distributed in β-phase. The mechanicals properties, that is hardness, ultimate tensile strength and compressive strength. It was found that the brass 60%Cu+39% Zn+1%Sn (precipitation hardening), all test mechanical properties it was higher than the all samples condition. This results can be explain incharacterization of microstructure to gives deformation of copper alloy. |
| Databáze: |
Supplemental Index |
| Externí odkaz: |
|