| Autor: |
Gopi, B., Naga Krishna, N., Sivaprasad, K., Venkateswarlu, K. |
| Zdroj: |
Advanced Materials Research; October 2012, Vol. 584 Issue: 1 p556-560, 5p |
| Abstrakt: |
The present work investigates the effect of rolling temperature on the mechanical properties and microstructural evolution of an Al-Mg-Si alloy with 3wt% TiB2 in-situ composite that was fabricated by stir casting route. The composite was rolled to a true strain of ≈0.7 at three different temperatures viz; room temperature (RT), liquid propanol (LP) and liquid nitrogen (LN) temperatures. Tensile tests revealed that the samples rolled at liquid nitrogen temperature exhibited improved properties compared to the samples rolled at other two temperatures. A tensile strength and ductility of 291 MPa and 8% respectively were exhibited by the liquid nitrogen rolled sample. The strength is observed to be ≈12% higher and ductility is ≈60% more when compared to the room temperature rolled sample. X ray diffraction peaks indicated that rolled samples exhibited considerable increase in peak broadening compared to the unrolled one, which is attributed to the increase of the lattice strain due to distortion and the decrease in grain size of the material. The enhanced mechanical properties of the liquid nitrogen rolled samples were attributed to the combined effect of grain refinement and accumulation of higher dislocation density. |
| Databáze: |
Supplemental Index |
| Externí odkaz: |
|