| Autor: |
Chen, Qing Jun, Hu, Lin Li, Zhou, Xian Liang, Hua, Xiao Zhen, Yang, Ying Jun |
| Zdroj: |
Advanced Materials Research; July 2011, Vol. 291 Issue: 1 p65-71, 7p |
| Abstrakt: |
The purpose of this study is to investigate the electrochemical properties of Fe44Cr16Mo16C18B6 amorphous alloy coating fabricated using high velocity oxygen fuel (HVOF) technology in 2.0M HCl and NaOH solution at room temperature(25oC). Based on the potentiodynamic polarization curves and Electrochemical Impedance Spectroscopy(EIS) testing results of coating in aqueous solutions of HCl and NaOH, the corrosion resistance of Fe44Cr16Mo16C18B6 amorphous alloy coating in HCl solution was superior to that in NaOH solution. The icorr was 1.487×10-5A·cm-2 in HCl solution and 1.107×10-4A·cm-2 in NaOH solution, while the Rt reach to 5.789×104Ω·cm2 and 9780Ω·cm2, respectively. On the other hand, these corrosion phenomenon could be better interpreted by R(Q(R(RQW)))(RL) and R(RL)(Q(R(CW))) equivalent circuit model, which were different from that of other Fe-based amorphous alloys in HCl and NaOH solution, respectively. |
| Databáze: |
Supplemental Index |
| Externí odkaz: |
|