Sakon, K., Hirokawa, Y., Masubuchi, Yasuji, Kikkawa, Shinichi |
| Zdroj: |
Materials Science Forum; October 2009, Vol. 631 Issue: 1 p327-331, 5p |
| Abstrakt: |
Sputter deposited Fe0.7Co0.3 nitride thin film had zinc blende structure. It was thermally decomposed completely back to the ferromagnetic Fe0.7Co0.3 alloy above 400°C. As-deposited nitride thin films obtained in cosputtering of (Fe0.7Co0.3)1-xAlx composite target with nitrogen sputter gas were solid solutions with zinc blende (x≤0.44) and wurtzite (x>0.5) type structure, respectively. The largest magneto resistance ratio of 0.24% was observed on the Fe0.7Co0.3 alloy particles dispersed in AlN thin film obtained by thermal decomposition of the nitride solid solution with x=0.66 at 500°C. |