| Autor: |
Gaki, Anna, Karavangelis, C., Kakali, Glykeria, Wiglusz, R.J., Strek, W. |
| Zdroj: |
Materials Science Forum; January 2010, Vol. 636 Issue: 1 p901-907, 7p |
| Abstrakt: |
La1-xSrxCoO3-δ (x=0, 0.2, 0.5) powders were prepared by a polymeric precursor route, with the application of microwave heating for the precursor preparation. Single-phase oxide powders are obtained after calcination at 700°C for x=0, 0.2 and 1300 °C for x=0.5. XRD, FTIR and TG-DTG measurements were used to examine the powder precursors as well as the intermediate and final products. SEM images indicated the small grain size of samples with x=0, 0.2. Conductivity and thermal expansion were measured by means of DC method and dilatometry respectively. The end member LaCoO3-δ showed a semiconducting behaviour, while doped samples showed a metallic behaviour at high temperatures. La0.8Sr0.2CoO3-δ showed the highest conductivity of all samples investigated, at temperatures higher than 300 °C. |