Goritskii, V. M., Terent'ev, V. F., Orlov, L. G., Balov, V. P., Shebatinov, M. P. |
| Zdroj: |
Strength of Materials; June 1975, Vol. 7 Issue: 6 p713-716, 4p |
| Abstrakt: |
Conclusions 1.At 77°K the fatigue crack develops along shear planes in individual parts of the propagated crack front.2.The more developed substructure of iron specimens previously fatigue-tested at 293°K promotes the formation of a more ductile fatigue fracture.3.In both the testing regimes investigated, the propagation of the fatigue crack in the stable growth stage takes up only an insignificant part (0.25%) of the total life of iron specimens at 77°K. |