Dentin permeability after pretreatment with titanium tetrafluoride and self-etching or universal adhesive systems.

Autor: Greco Franco, Gabriel, de Moraes Cardoso, Ruthinea Faria, Russo Carlos, Natália, Pedroso Turssi, Cecilia, Botelho do Amaral, Flávia Lucisano, Gomes França, Fabiana Mantovani, Tarkany Basting, Roberta
Předmět:
Zdroj: Brazilian Journal of Oral Sciences; 2023, Vol. 22, p1-9, 9p
Abstrakt: Aim: To evaluate dentin permeability after pretreatment with 2.5% aqueous solution of titanium tetrafluoride (TiF4), followed by a self-etching universal adhesive system. Methods: Forty dentin discs (1.5 mm thick) were randomly divided into groups according to the application or non-application of a pretreatment, and the type of adhesive system to be tested (two-step self-etching/ Clearfil SE Bond/ Kuraray Medical, or universal adhesive system/ Single Bond Universal/ 3M ESPE). Both sides of the discs were conditioned with 37% phosphoric acid to remove the smear layer. The first hydraulic conductivity measurement (L1) was performed in a permeability machine, under 5 PSI pressure. The samples were sanded again to form a standardized smear layer. The teeth designated for pre-treatment with TiF4 received the TiF4 solutions applied actively for 60 seconds, and the adhesive systems were applied according to the manufacturer's instructions. Then, a new hydraulic conductivity measurement (L2) was performed for the purpose of calculating the hydraulic conductance at a later time, considering the water viscosity and the thickness of the specimen. The percentage (L) of dentin permeability after application of the adhesive system was obtained (L (%) = [(L1-L2) x100] / L1). The Mann-Whitney non-parametric test was applied. Results: There was no difference between the two adhesive systems, or between the groups with or without pretreatment, as regards dentin permeability (p>0.05). Conclusion: Pretreatment with 2.5% TiF4 did not influence dentin permeability, irrespective of the adhesive system used. [ABSTRACT FROM AUTHOR]
Databáze: Supplemental Index