Influence of In-Service Degradation on Strain Localization in Steel of Main Gas Pipelines.

Autor: Maruschak, Pavlo, Bishchak, Roman, Panin, Sergey, Pylypenko, Andriy, Menou, Abdellah, Danyliuk, Iryna
Předmět:
Zdroj: AIP Conference Proceedings; 2014, Vol. 1623, p399-402, 4p, 1 Chart, 1 Graph
Abstrakt: General regularities in the failure kinetics of steel of main gas pipelines (17GS) are established using the method of complete stress-strain curves, meanwhile in-service degradation of metals is taken into account. The influence of material degradation on material properties under static tensioning is considered using two independent approaches: the phenomenological model of damage accumulation in metals, and the fractographic analysis method. The accumulation of in-service damage is found to increase a degree of material opening and lead to partial "embrittlement" of the steel matrix due to the microdefects accumulation in the vicinity of metal cracking caused by hydrogenation. [ABSTRACT FROM AUTHOR]