Kunshina, G., Gromov, O., Lokshin, E., Kalinnikov, V. |
Zdroj: |
Russian Journal of Inorganic Chemistry; May2014, Vol. 59 Issue 5, p424-430, 7p |
Abstrakt: |
A modified sol-gel process was studied as applied to synthesize a lithium-conducting solid electrolyte of composition LiAlTi(PO) (LATP) using water-soluble salts Al(NO) · 9HO, LiNO · 3HO, and (NH)HPO and a titanium(IV) citrate complex. As-synthesized samples were characterized using X-ray powder diffraction, DSC/TG, SEM, and impedance spectroscopy. Sintering of as-synthesized amorphous powders at 700°C was found to yield LATP with crystallite sizes of 42-48 nm. Ionic conductivity of the electrolyte measured in the frequency range 25-10 Hz in disks having 86-90% density that were sintered at 1000°C was (3-4) × 10 S/cm. Temperature-dependent ionic conductivity was studied in the range 25-200°C. The activation energy of conduction was determined for LATP. [ABSTRACT FROM AUTHOR] |