Effect of adhesive application on the shear bond strength of refrigerated and pre-heated of different composite resins to orthodontic molar tubes.

Autor: Lobato, María, Montero, Javier, Fuentes, M. Victoria, Albaladejo, Alberto
Předmět:
Zdroj: Journal of Adhesion Science & Technology; Nov2013, Vol. 27 Issue 20, p2251-2264, 14p, 3 Diagrams, 2 Charts, 1 Graph
Abstrakt: Objective: To evaluate the effect of adhesive application on the shear bond strength (SBS) of orthodontic tubes to acid-etched human enamel using different temperatures and orthodontic composite resins.Methods: One hundred and twenty metal tubes were bonded to human third molars, which were randomly divided into three groups depending on the composite used: Transbond XT (XT); Transbond Supreme LV (LV); and Light Bond (LB). Each group was divided into four subgroups depending on the temperature (5°, 20°, 40°, and 60°) applied to the composite before cementing. For each experimental subgroup, half the specimens were bonded in combination with XT Primer. After 72 h, a SBS test was performed using a universal testing machine. Statistical analysis was performed using ANOVA,post hocintergroup comparisons, chi-square test, and linear regression. Two representative molar surfaces from each subgroup were assessed under Scanning electron microscope.Results: The composite type only influenced XT regarding LB. The use of adhesive does not affect the SBS values of any composite. The flowable composites with adhesive containing zirconia (LV) as a filler showed lower SBS when cooled to 5 °C and when increases the temperature from 40 °C. Whether adhesive was used or not, composites with silica as filler (LB) showed lower SBS at 60 °C and increased to 5 °C.Conclusions: For all composites, from 20 °C, SBS values tend to increased and started to decline at 40°C except when adhesive is applied to the quartz-filled composite, which continues to increase, and the silica-filled composite without adhesive, which tend to decreases from 5 °C. [ABSTRACT FROM PUBLISHER]
Databáze: Complementary Index
Externí odkaz:
Nepřihlášeným uživatelům se plný text nezobrazuje