KHORUNOV, V. F., ZVOLINSKY, I. V., MAKSYMOVA, S. V. |
| Předmět: |
|
| Zdroj: |
Paton Welding Journal; Apr2013, Issue 4, p21-25, 5p |
| Abstrakt: |
The article is dedicated to investigation of the process of arc brazing on thin-sheet steel 08kp (rimmed) by using brazing filler alloy BrKMts 3-1. Peculiarities of spreading of the filler alloy under conditions of tungsten-electrode arc heating using different shielding atmospheres are considered. It is shown that the best spreading is achieved in a mixture of argon with 10 wt.% of hydrogen. Heat input in arc welding and brazing was compared by the calculation method: the values of heat input (for a specific case) were 1200 and 516.7 J/cm, respectively. The possibility of decreasing the heat input by using the pulsed process is shown. Peculiarities of formation of butt and overlap joints are revealed. In brazing of the butt joints the gap can be adjusted over wide ranges (0.2-0.8 mm), and in brazing of the overlap joints this parameter is within the narrower ranges. However, in general the use of the overlap joints seems more promising. As seen from the data of optical microscopy and X-ray spectrum microanalysis, a silicide interlayer forms at the interface of the joint, where the content of silicon may exceed 10 wt.%. Structure of the seam is a solid solution with discrete precipitates of the phase with the increased silicon content along the grain boundaries. It is shown that in brazing under optimal conditions the strength value of the butt joints on low-carbon steel brazed by using filler alloy BrKMts 3-1 is 330-390 MPa. In the overlap joints the full strength value is achieved at an overlap equal to thickness of the materials joined. 11 Ref., 8 Figures. [ABSTRACT FROM AUTHOR] |
| Databáze: |
Complementary Index |
| Externí odkaz: |
|