Autor: |
Zhao, Li, Chen, Bai-Shuang, Zhang, Jia-Lin, Wang, Dian-Long |
Předmět: |
|
Zdroj: |
Journal of Solid State Electrochemistry; Jun2012, Vol. 16 Issue 6, p2079-2084, 6p |
Abstrakt: |
A solid film was prepared by electrodepositing on a gold-film-coated quartz crystal electrode in NaFeO solution, and characterized in 1 M LiClO/propylene carbonate (PC) + 1, 2-dimethoxyethane (DME; 1:1 by volume) electrolyte using electrochemical quartz crystal microbalance (EQCM). The EQCM experimental and X-ray photoelectron spectroscopy results indicate that the composition of the electrodeposited solid film prepared in the potential range of 0.18 to −0.57 V vs. Ag/AgCl is FeOOH; and almost 1 mol lithium ions can be intercalated into and then extracted from 1 mol FeOOH film during discharge/charge process in 1 M LiClO/PC + DME electrolyte. The discharge/charge experiment indicates that the specific capacity of FeOOH film stabilizes at a value close to its theoretical specific capacity after 20 cycles, and FeOOH film maintains a specific capacity of about 300 mAh g at the end of 170 cycles. It is therefore concluded that the FeOOH film has a good electrochemical cycle ability in 1 M LiClO/PC + DME electrolyte. [ABSTRACT FROM AUTHOR] |
Databáze: |
Complementary Index |
Externí odkaz: |
|