| Abstrakt: |
A late porogen removal scheme was used to make low-k materials (k = 2.72 to 2.02) using methylsilsesquioxane (MSQ) and a high-temperature porogen, poly(styrene-b-4-vinylpyridine) (PS-b-P4VP), to circumvent the reliability issues related to as-deposited porous dielectric. Based on the nanoindentation and Fourier transform infrared spectroscopy (FTIR) analysis, the moduli of the hybrid films were found to be higher than their porous forms, and even better than the dense MSQ film, for porogen loading below a critical level (~69.5 vol%). This could be attributed to their enhanced degree of cross-linking in MSQ as evidenced by the network/cage structural ratios. Besides, high-temperature porogen plays different roles during the cross-linking of MSQ depending on its loadings. In this study, with immediate loading at 16.7 vol%, PS-b-P4VP can serve as plasticizer to enhance the degree of cross-linking, but at a large loading >16.7 vol%, it becomes a steric hindrance reducing the degree of cross-linking. [ABSTRACT FROM AUTHOR] |