Autor: |
Vaish, Rahul, Varma, K. B. R. |
Předmět: |
|
Zdroj: |
Journal of Applied Physics; Dec2009, Vol. 106 Issue 11, p114109-1-114109-5, 5p, 7 Graphs |
Abstrakt: |
X-ray powder diffraction along with differential thermal analysis carried out on the as-quenched samples in the 3BaO–3TiO2–B2O3 system confirmed their amorphous and glassy nature, respectively. The dielectric constants in the 1 kHz–1 MHz frequency range were measured as a function of temperature (323–748 K). The dielectric constant and loss were found to be frequency independent in the 323–473 K temperature range. The temperature coefficient of dielectric constant was estimated using Havinga’s formula and found to be 16 ppm K-1. The electrical relaxation was rationalized using the electric modulus formalism. The dielectric constant and loss were 17±0.5 and 0.005±0.001, respectively at 323 K in the 1 kHz–1 MHz frequency range which may be of considerable interest to capacitor industry. [ABSTRACT FROM AUTHOR] |