| Autor: |
de Assis OlImpio Cabral, Francisco, de Araujo Machado, Fernando Luis, de Araujo, José Humberto, Soares, João Maria, Ricalde Rodrigues, Alexandre, Araujo, Armando |
| Předmět: |
|
| Zdroj: |
IEEE Transactions on Magnetics; Nov2008 Part 2 of 2, Vol. 44 Issue 11, p4235-4238, 4p, 7 Graphs |
| Abstrakt: |
Fern-ferromagnetic nanocomposites CoFe2O4-CoFe2 were prepared via reduction of the cobalt ferrite CoFe2O4 into a hydrogen atmosphere and by heat treatments. This preparation method yielded powders with relative volume fraction of CoFe2O4 and CoFe2 in the range 0-0.91. The structure and the room temperature magnetization of the samples were analyzed by X-ray diffraction, scanning electron microscope (SEM) and transmission electron microscope (TEM), and by vibrating sample magnetometry, respectively. It was found that the saturation magnetization of the nanocomposite powders increases with the volume fraction of the ferromagnetic phase while their coercivity decreases. The highest value (5 kJ/m³) for the maximum energy product (BH)max was obtained for the sample containing 91% in volume of CoFe2. This (BH)max is 19% higher than the value measured in pure CoFe2O4. The magnetic field dependence of the magnetization did also behave as the nanocomposite powders were single-phase materials. This result indicates that the hard ferrimagnet CoFe2O4 and the soft ferromagnet CoFe2 are effectively exchange coupled and that their magnetization reverses cooperatively in the range of compositions investigated. [ABSTRACT FROM AUTHOR] |
| Databáze: |
Complementary Index |
| Externí odkaz: |
|