Synthesis, Magnetic, and Photocatalytic Activity of Polypyrrole-Based TiO 2 –Fe Catalyst for Wastewater Treatment.

Autor: Nazir, Muhammad Khalid, Javaid, Sana, Afzal, Hina, Taj, Muhammad Babar, Baamer, Doaa F., Almasoudi, Afaf, Aldahiri, Reema H., Ali, Omar Makram, Khan, Muhammad Imran, Ahmed, Muhammad Mahboob, Shanableh, Abdallah, Fernandez-Garcia, Javier
Předmět:
Zdroj: Catalysts (2073-4344); Oct2024, Vol. 14 Issue 10, p692, 22p
Abstrakt: The primary aim of this study is to investigate the degradation efficacy of the Ppy/TiO2-Fe photocatalyst for MB dye in an aqueous solution. Firstly, the direct addition of TiO2 and Fe was done to prepare Ppy/TiO2-Fe photocatalyst. Fourier transformation infrared spectroscopy, XRD, SEM, BET surface area analysis, and magnetization tests established the formation of the Ppy/TiO2-Fe photocatalyst. The crystallite sizes of TiO2, Fe-TiO2, and Ppy/TiO2-Fe photocatalyst were estimated to be 24.99 nm, 21.94 nm, and 21.84 nm, respectively. For the synthesis confirmation, the FTIR spectrum confirmed the existence of Ti-O, Fe-O, and Ppy-related bonds. While comparing the SEM images, the impact of polypyrrole on the particle shape was observed with less aggregation and increased surface roughness. The VSM analysis revealed that incorporating polypyrrole (Ppy) into Fe-TiO2 significantly enhances its magnetic properties, with Ppy/TiO2-Fe exhibiting superparamagnetic behavior, characterized by a higher saturation magnetization (Ms) of 33.11 emu/g and a lower coercivity (Hc) of 0.160 Oe, compared to Fe-TiO2's Ms of 1.09 emu/g and Hc of 341.39 Oe. The N2 sorption desorption, with a specific surface area of 2.25 × 102 m2/g, is beneficial for photocatalytic activity. The concentration of dye, amount of catalyst, pH, and temperature were studied to evaluate the photocatalytic efficiency of the synthesized Ppy/TiO2-Fe photocatalyst under different conditions. The findings revealed a degradation efficiency of 91.92%. The degradation rate reached 91.92% under optimal conditions within 120 min and could be fitted well by first-order kinetics. The photocatalytic efficiency was also evaluated for the scavenger, and the concentration of H2O2 and the reusability of the catalyst were demonstrated. Based on the observed results, the Ppy/TiO2-Fe photocatalyst could be applied more effectively and efficiently to photocatalytic degradation of organic dyes in wastewater treatment. [ABSTRACT FROM AUTHOR]
Databáze: Complementary Index
Externí odkaz:
Nepřihlášeným uživatelům se plný text nezobrazuje