| Abstrakt: |
The reduction of carbon footprint, the recycling of agricultural waste, and the development of novel environmentally friendly building materials are urgent matters that necessitate innovative solutions. The objective of this study is to explore the feasibility of utilizing banana leaf ash (BLA) as a partial substitute for cement in conventional density concrete technology. The BLA-modifying additive was produced under laboratory conditions. Its chemical, phase and granulometric composition was assessed. To determine the degree of effectiveness of BLA, eight concrete compositions were developed, where the BLA content varied from 0% to 14% with an interval of 2%. The properties of fresh concrete, such as density and slump, as well as compressive strength, flexural strength, water absorption, and microstructure of hardened concrete, were studied. It has been determined that the BLA additive exhibits pozzolanic activity, with a SiO2 content of 50.83%. It is recommended that the replacement of cement with BLA does not exceed 10% for optimal results. Concrete modified with 6% BLA had the best properties and structure. The study revealed a significant 7.42% increase in compressive strength, a 7.01% increase in flexural strength, and a notable 9.28% decrease in water absorption. Thus, the obtained result proves the possibility of using BLA as a modifying additive in the technology of cement composites. The developed concrete has improved properties and is a more environmentally friendly building material than conventional concrete. [ABSTRACT FROM AUTHOR] |