| Abstrakt: |
This paper deals with the bonding characteristics of cross-laminated timber (CLT) panels made of Silver birch (Betula pendula Roth.), European aspen (Populus tremula L.), and Norway spruce (Picea abies (L.) H. Karst.) wood. Three-layered single-species CLT panels were manufactured using birch, aspen, and spruce lamellae bonded with a one-component polyurethane (PUR) adhesive. Spruce CLT panels were used as reference. The bonding characteristics of CLT were assessed based on bond shear strength, total and maximum delamination, and wood failure percentage. The reference spruce CLT met both criteria (Delamtot ≤ 10%, Delammax ≤ 40%) for passing the delamination test, where up to 80% of the test samples passed. The aspen and birch CLTs met the criterion for maximum delamination (26.5% and 33.2%, respectively), but exceeded the maximum allowed value for total delamination (12.7% and 13.2%, respectively). However, the minimum requirement of 70% wood failure percentage (WFP) was met for all CLT types, with aspen CLTs achieving 83.7% and birch CLTs 76.9%. The spruce CLTs achieved an average bond shear strength of 1.9 N/mm2, while both hardwood CLTs had significantly higher values, with the aspen CLT at 3.3 N/mm2 and the birch CLT at up to 3.9 N/mm2. Based on the results obtained, it can be concluded that cross-laminated timber (CLT) made from hardwoods like aspen and birch is suitable for environments with low humidity fluctuations. [ABSTRACT FROM AUTHOR] |