Friction stir processing (FSP) manufacturing technology was used to fabricate medium Mn advanced high-strength steel in this study. The mechanical properties and microstructure of the steel fabricated using FSP were investigated. The steel obtained a total elongation of 35.1% and a tensile strength of 1034.6 MPa, which is about 59% higher than that of the steel without FSP. After FSP, a gradient structure occurs along the thickness direction. Specifically, across the thickness direction from the base material zone to the transition zone and finally to the stirring zone, both the grain size and austenite fraction decrease while the dislocation density increases, which results from the simultaneous effect of severe plastic deformation and recrystallization during FSP. Due to the gradient structure, an obvious difference in the strain across the thickness direction of the steel occurs during the deformation process, resulting in significant hetero-deformation-induced (HDI) strengthening. The deformation mechanism analysis reveals that HDI strengthening and dislocation strengthening are the main factors in the improvement in the strength–ductility balance. The obtained knowledge sheds light on the process of fabricating medium Mn steels with excellent properties using FSP manufacturing technology. [ABSTRACT FROM AUTHOR] |
| Databáze: |
Complementary Index |
| Externí odkaz: |
|