| Abstrakt: |
This study investigates the enhancement of wear resistance in CuCrZr rails through the plasma cladding of CuCrZr-GO coatings with a varying graphene oxide (GO) content. The microstructure, phase composition, and mechanical properties of CuCrZr coatings containing 0%, 0.2%, 0.4%, 0.6%, and 0.8% GO were examined using scanning electron microscopy (SEM), X-ray diffraction (XRD), ESD surface scanning, friction and wear tests, and hardness analysis. The findings indicated that increasing the GO content from 0% to 0.6% results in a transition in the coating microstructure from columnar to equiaxed crystals, leading to an improved density. However, at 0.8% GO, numerous porosity defects were observed. The coating containing 0.6% graphene oxide (GO) exhibited a superior performance, with a hardness of 75, a friction coefficient of approximately 0.7, and a wear mass of 2.84 mg under a 10 N load. In comparison to the CuCrZr coating lacking GO, the hardness showed an increase of around 4.8%, the friction coefficient decreased by approximately 5.1%, and the wear mass diminished by 59.4%. These findings hold significant implications for extending the operational lifespan of electromagnetic railguns. [ABSTRACT FROM AUTHOR] |