Odontology; Jan2024, Vol. 112 Issue 1, p74-82, 9p |
| Abstrakt: |
Because the use of hydrofluoric acid (HF) poses health risks if handled improperly, many clinicians prefer to have the ceramic restorations pre-etched in dental laboratories. However, during the try-in procedure, the pre-etched glass–ceramic restorations may be contaminated with saliva resulting in reduced bond strength. This in-vitro study aimed to investigate the effect of different surface treatments on the bond strength of lithium disilicate (LD) glass–ceramic restorations (IPS e.max Press, Ivoclar Vivadent) to two resin cements. One-hundred eighty blocks (4X4X3mm) of LD glass–ceramic were divided into twelve groups (n = 15), of which six received Variolink Esthetic DC (VE) cement and six received RelyX Ultimate (RU) cement, following the surface treatments: G1) Control: Hydrofluoric Acid + Silane (HF + Sil); G2) Hydrofluoric Acid + Saliva + Silane (HF + S + Sil); G3) Hydrofluoric Acid + Saliva + Ivoclean + Silane (HF + S + IC + Sil); G4) Hydrofluoric Acid + Saliva + Phosphoric Acid + Silane (HF + S + P + Sil); G5) Hydrofluoric Acid + Saliva + Monobond Etch & Prime (HF + S + EP); G6) Monobond Etch & Prime (EP). Following treatment, a resin-cement cylinder (2.3 mm diameter) was built on the glass–ceramic surface, photocured (20 s), stored in distilled water (37 °C, 24 h) and submitted to the shear bond strength test. Bond strength data (MPa) were subjected to two-way ANOVA and Tukey (α = 0.01). Cement type and surface treatment had a significant effect on the bond strength (p < 0.001) (Table 4). Single-step Monobond Etch & Prime (EP) significantly improved the bond strength of resin-cements to glass–ceramic with and without saliva contamination. [ABSTRACT FROM AUTHOR] |
| Databáze: |
Complementary Index |
| Externí odkaz: |
|
Full text from SpringerLink