Assessment of the Pitting, Crevice Corrosion, and Mechanical Properties of Low-Temperature Plasma-Nitrided Inconel Alloy 718.

Autor: Nuñez de la Rosa, Yamid, Palma Calabokis, Oriana, Ballesteros-Ballesteros, Vladimir, Tafur, Cristian Lozano, Borges, Paulo C.
Předmět:
Zdroj: Metals (2075-4701); Jul2023, Vol. 13 Issue 7, p1172, 19p
Abstrakt: A comparative study on the mechanical properties, scratch resistance, and localized corrosion (pitting and crevice) of plasma-nitrided Inconel alloy 718 (UNS NO7718: IN 718) was carried out. Thermochemical treatment was performed at low temperatures (400 and 450 °C) for 4 h. The treatment formed layers with thicknesses of 7.17 ± 0.89 µm (400 °C) and 7.96 ± 0.48 µm (450 °C). The XRD and nanohardness analyses indicated the formation of a hard layer composed of the expanded austenite phase (γN), CrN at 400 °C, and CrN + γ at 450 °C, with a maximum indentation hardness of 12 and 12.5 GPa, respectively, when compared to the 5 GPa substrate hardness. The scratching tests (2–8 N) showed that with increasing load, the nitrided surfaces had a transition from 100% microcutting to a combination of microplowing/cutting, with the presence of cracks. The critical load of the nitrided surfaces was 3 N for 400 °C and 4 N for 450 °C. The untreated condition maintained a crack-free combined mechanism regardless of the load. For the same load, the nitrided surfaces held lower coefficient of friction values and higher scratch resistance values, which were more pronounced at 450 °C. The linear polarization tests (3.56 wt.% NaCl) showed pitting corrosion in all samples, with the 450 °C condition being less resistant. Nitriding at 400 °C increased the crevice corrosion resistance of Inconel, while at 450 °C, it severely damaged it. Nitriding at 400 °C brought concomitant gains in hardness and scratch and crevice corrosion resistance when compared to the as-received IN 718. [ABSTRACT FROM AUTHOR]
Databáze: Complementary Index