This study reports on the as-cast microstructures of AlCrFeMnV, AlCrFeTiV, and AlCrMnTiV equimolar multi-principal element alloys. Thermodynamic modeling predicts that these alloys solidify as BCC solid solutions, with additional phases forming at lower temperatures. We present the measured densities, the elastic modulus values measured by nanoindentation, and the Vickers microhardness of the alloys. These properties are correlated to the underlying microstructures, as measured by x-ray diffraction, scanning electron microscopy, and atom-probe tomography. The densities of the alloys range from 5.53 to 6.42 × 10 3 kg m − 3 . The elastic modulus of AlCrFeMnV, AlCrFeTiV, and AlCrMnTiV are 211, 194, and 175 GPa, respectively, and their Vickers microhardness values are 3.9, 6.1, and 5.7 GPa, respectively. After arc-melting, AlCrFeMnV and AlCrFeTiV are BCC solid solutions while AlCrMnTiV has two phases: a BCC phase and a minor hexagonal C14 Laves phase that is enriched in V and Cr. [ABSTRACT FROM AUTHOR] |