Bulavchenko, Olga A., Konovalova, Valeriya P., Saraev, Andrey A., Kremneva, Anna M., Rogov, Vladimir A., Gerasimov, Evgeny Yu., Afonasenko, Tatyana N. |
| Předmět: |
|
| Zdroj: |
Catalysts (2073-4344); Jan2023, Vol. 13 Issue 1, p57, 15p |
| Abstrakt: |
MnOx-ZrO2 catalysts prepared by co-precipitation and vacuum impregnation were calcined at 400–800 °C and characterized by powder X-ray diffraction, textural studies, high-resolution transmission electron microscopy, temperature-programmed reduction, X-ray absorption near edge structure, and X-ray photoelectron spectroscopy. The catalytic activity was tested in the CO oxidation reaction. The activity of the co-precipitated samples exceeds that of the catalysts prepared by vacuum impregnation. The characterization studies showed that the nature of the active component for the catalysts obtained by co-precipitation differs from that of the catalysts obtained by impregnation. In the impregnation series, the most active catalyst was obtained at a temperature of 400 °C; its increased activity is due to the formation of MnO2 oxide nanoparticles containing Mn4+ and low-temperature reducibility. An increase in the synthesis temperature leads to the formation of less active Mn2O3, catalyst sintering, and, accordingly, deterioration of the catalytic properties. In the case of co-precipitation, the most active CO oxidation catalysts are formed by calcination at 650–700 °C in air. In this temperature interval, on the one hand, a MnyZr1−yO2−x solid solution is formed, and on the other hand, a partial separation of mixed oxide begins with the formation of highly dispersed and active MnOx. A further increase in temperature to 800 °C leads to complete decomposition of the solid solution, the release of manganese cations into Mn3O4, and a drop in catalytic activity. [ABSTRACT FROM AUTHOR] |
| Databáze: |
Complementary Index |
| Externí odkaz: |
|
|
Nepřihlášeným uživatelům se plný text nezobrazuje |
K zobrazení výsledku je třeba se přihlásit.
|