Aremu, O. H., Akintayo, C. O., Nelana, S. M., Klink, M. J., Ayanda, O. S. |
| Předmět: |
|
| Zdroj: |
Nature Environment & Pollution Technology; Dec2022, Vol. 21 Issue 4, p1875-1885, 11p |
| Abstrakt: |
This study examined the synthesis of a viable catalyst for the degradation of metronidazole contained in aquaculture effluent. Zinc oxide nanoparticles (n-ZnO) were synthesized via the precipitation method and calcined at 500oC in a muffle furnace to enhance the degradability properties. The morphology showed a hexagonal structure with an average particle size of 71.48 nm and the elemental composition showed a higher weight percent of 59.15% for zinc and 21.65% for oxygen. The FTIR confirms the vibrational characteristic mode of the Zn-O band at 427.21cm-1. The XRD showed a good crystallinity and the BET surface area was 8.58 m².g-1 which showed that the n-ZnO possesses more active sites that can remove pollutants from wastewater. However, no studies have been done on the removal of MNZ in aquaculture effluent. The kinetics followed pseudo-second-order kinetics and the Langmuir- Hinshelwood model best fit the degradation process with R², Kc, and KLH values of 0.96781, 1.486 × 10-1 mg. Lmin-1) and 8.790 × 10-2 (L.mg-1). Under the influential parameters, the percentage COD removal achieved for MNZ in aquaculture effluent was 62.6%, 89.8%, and 98.5% of MNZ at 20% ultrasonic amplitude, 5 mL 2% H2O2 and 0.02g n-ZnO within 60 min sonication time for US only, US/n-ZnO and US/n-ZnO/H2O2 systems. Hence, MNZ contained in aquaculture effluent can best be degraded with the synergetic effect of the US/n-ZnO/ H2O2 system. [ABSTRACT FROM AUTHOR] |
| Databáze: |
Complementary Index |
| Externí odkaz: |
|