| Autor: |
Guishen, Yu, Xin, Chen, Zitao, Wu |
| Předmět: |
|
| Zdroj: |
Journal of Adhesion; 2022, Vol. 98 Issue 11, p1663-1686, 24p |
| Abstrakt: |
This paper introduced a hybrid joining system including friction stir spot welding (FSSW) and adhesive bonding, named friction stir spot weld bonding (FSSWB). In order to avoid adhesive layer carbonization, FSSWB was processed by flow-in method. The aim of this study was to evaluate the effect of adhesive ductility and joint configuration on the tensile-shear performances of AA6061 aluminum alloy. Two types of adhesives were considered: brittle epoxy (AV138) and ductile epoxy (Araldite 2015). Besides, hybrid joints involve three types of joint configurations (AV138, Araldite 2015 and dual adhesive). A finite element (FE) model of hybrid joints failure process was established based on the extended finite element method (XFEM) and cohesive zone model (CZM). The tensile-shear failure load (TSFL) prediction values and joint failure process were in good agreement with the experiments. Compared to FSSW, the TSFL values for the three types of hybrid joint increased by 166.5%, 294.8% and 173.8% respectively. In addition, the stresses at the hook tip of the three hybrid joints were decreased by 85.56%, 79.31% and 83.67%. From the study, it was found that the use of ductile adhesives at two sides of joint was more helpful to increase the load-bearing capacity of FSSWB joints. [ABSTRACT FROM AUTHOR] |
| Databáze: |
Complementary Index |
| Externí odkaz: |
|