Rapid synthesis and magnetic property characterization of Mg2+ doped Co3O4 nanostructures.

Autor:	Sundararajan, M., Vidhya, J., Revathi, R., Sukumar, M., Arunadevi, B., Rajkumar, R., Ramachandran, S., Kamalakannan, M., Dash, Chandra Sekhar, Rajabathar, Jothi Ramalingam, Arokiyaraj, Selvaraj
Předmět:	MAGNETIC properties CRYSTAL grain boundaries NANOSTRUCTURES SPINEL X-ray diffraction OXYGEN carriers
Zdroj:	Inorganic & Nano-Metal Chemistry; 2022, Vol. 52 Issue 7, p996-1002, 7p
Abstrakt:	Utilizing combustion method Mg substituted Co3O4 nanoparticles were prepared using the fuel L-alanine. The formation of the cubic spinel structure in the prepared undoped Co3O4 and Mg substituted Co3O4 is assured by X-ray diffraction (XRD) studies. The average crystallite size was observed to lie within 48.6 nm to 17.3 nm. The microstructural analysis shown that the prepared nanoparticles are porous in nature comprising of intragranular pores and melded grains with distinct grain boundaries. The bandgap values were determined using Kubelka–Munk (K–M) technique which was found to fall within 1.87–3.64 eV range. Interestingly, para-/superpara- magnetic characteristics was seen at ±15KOe by the magnetic studies. The FT-IR bands at 662 and 569 cm−1are attributed to the Co–O stretching mode of cubic spinel Co3O4 structure for the prepared samples.. [ABSTRACT FROM AUTHOR]
Databáze:	Complementary Index
Externí odkaz:	Zobrazit plný text záznamu Plný text ve formátu HTML
Nepřihlášeným uživatelům se plný text nezobrazuje	K zobrazení výsledku je třeba se přihlásit.