AIP Conference Proceedings; 2020, Vol. 2347 Issue 1, p1-6, 6p |
| Abstrakt: |
In this study, poly (methyl methacrylate)/palm kernel shell (PMMA/PKS) composites were prepared by solution casting. The effect of solvent to matrix (S/M) weight ratio and stearic acid (SA) treatment on PMMA/PKS composites were studied. PMMA pellets were dissolved and PKS powders were dispersed into acetone, separately. PMMA solution and PKS suspension were then mixed in ultrasonic bath. The mixture was then poured into a glass petri dish to evaporate acetone at room temperature and finally PMMA/PKS composite thin film was obtained. PMMA/PKS composites were characterized by using SEM and were subjected to tensile test. It was found that tensile strength, modulus of elasticity of composite increased but elongation at break decreased with the increasing S/M ratio and with SA treatment. The improvement of the mechanical properties was due to the improved interfacial bonding following the SA treatment and the formation of crystallized PMMA domain in the composite with the increasing S/M ratio. SEM images revealed even fracture surfaces as S/M increased and with the application of SA treatment that indicate better matrix-filler adhesion. It can be concluded that S/M increment and SA treatment improved mechanical properties of PMMA/PKS composite. [ABSTRACT FROM AUTHOR] |
| Databáze: |
Complementary Index |
| Externí odkaz: |
|