| Autor: |
Emilia, VISILEANU, Laura, CHIRIAC, Razvan, SCARLAT, Alina, VLADU |
| Předmět: |
|
| Zdroj: |
Annals of the University of Oradea. Fascicle of Textiles, Leatherwork; 2021, Vol. 22 Issue 1, p89-94, 6p |
| Abstrakt: |
Composite textile structures designed to repair parietal defects, were obtained from monofilament yarns of polyester, polylactic acid and multifilament of Ag and high-density polyethylene, on Shima Seiki SIG 123 knitting machine of E8 gauge. The mass of composite structures after finishing is placed between 29.6 g/m2 and 158.9 g/m2. The textile structures from: PES/Ag and PP/Ag belong to low elastic modulus meshes (<10.9MPa - specific to the abdominal fascia) and those from: PES/PE and PES/PLA belong to high elastic modulus meshes (>10.9MPa). The anisotropy is suitable for all variants of textile structures with values less than 1.00. The best value of cell proliferation indicator - MTT (1,771) was recorded at the PES/PLA composite textile structure which is higher than the control value of 1.22; this structure also shows the lowest value of cell death indicator - LDH (0.405), but which is higher than the control value of 0.370; cell viability has a very high level in this structure (144.83%), higher than that observed in control cells (HT 29 cells in culture) of 100%. [ABSTRACT FROM AUTHOR] |
| Databáze: |
Complementary Index |
| Externí odkaz: |
|