Saleem, Mehvish, Zahid, Saba, Ghafoor, Sarah, Khalid, Hina, Iqbal, Haffsah, Zeeshan, Rabia, Ahmad, Sarfraz, Asif, Anila, Khan, Abdul Samad |
| Předmět: |
|
| Zdroj: |
Journal of Applied Polymer Science; 5/10/2021, Vol. 138 Issue 18, p1-16, 16p |
| Abstrakt: |
This study aimed to synthesize experimental composites reinforced with various concentrations (0, 40, 50, and 60 wt%) of nano‐hydroxyapatite grafted glass fibers. The release of monomers, residual monomers, and in‐vitro bioactivity of composite groups were evaluated after 1, 7, and 28 days. Compressive strength/ modulus, cell viability (by direct and indirect method), and bacterial adhesion were evaluated. The results showed that bis‐GMA was released from all samples. TEGDMA released from 50 and 60 wt% samples on day 1 and UDMA showed negligible release. Compressive strength values of 40 wt% sample were higher than other experimental groups. New apatite layer was formed, whereby both direct and indirect methods demonstrated cell viability. The numbers of active colonies grown were least for 60 wt% sample while their number increased over time. The nano‐hydroxyapatite/glass fibers have potential to be used as filler in dental composites and experimental composites were found to be biocompatible and comparable with commercial material. [ABSTRACT FROM AUTHOR] |
| Databáze: |
Complementary Index |
| Externí odkaz: |
|
Plný text