| Autor: |
Atif A Khan, E Repiso, M Herrera, P J Carrington, M de la Mata, J Pizarro, A Krier, S I Molina |
| Předmět: |
|
| Zdroj: |
Nanotechnology; 3/6/2020, Vol. 31 Issue 10, p1-1, 1p |
| Abstrakt: |
Sub-monolayer (SML) deposition of InSb within InAs matrix by migration enhanced epitaxy tends to form type II SML nanostructures offering efficient light emission within the mid-infrared (MIR) range between 3 and 5 μm. In this work, we report on the Sb distribution in InSb/InAs SML nanostructures with InAs cap layers grown at temperatures lower than that associated with the under-grown InSb active layer. Analysis by transmission electron microscopy (TEM) in 002 dark field conditions shows that the reduction in the growth temperature of the InAs cap layer increases the amount of Sb deposited in the layers, in good agreement with the x-ray diffraction results. TEM micrographs also show that the layers are formed by random InSbAs agglomerates, where the lower cap temperature leads to a more continuous InSb layer. Quantitative atomic column resolved high angle annular dark field-scanning (S)TEM analyses also reveal atomic columns with larger composition of Sb for the structure with the lowest InAs cap layer temperature. The dependence of the Sb distribution on InAs cap growth temperature allows tuning the corresponding emission wavelength in the MIR range, as shown by the photoluminescence emission spectra. [ABSTRACT FROM AUTHOR] |
| Databáze: |
Complementary Index |
| Externí odkaz: |
|