| Autor: |
Kireeva, Irina, Chumlyakov, Yury, Vyrodova, Anna, Pobedennaya, Zinaida, Poklonov, Vyacheslav, Bessonova, Irina, Kuksgauzen, Dmitriy |
| Předmět: |
|
| Zdroj: |
AIP Conference Proceedings; 2019, Vol. 2167 Issue 1, p020159-1-020159-4, 4p, 1 Diagram, 2 Graphs |
| Abstrakt: |
The effect of γ′-phase particles on the mechanical behaviour was studied in single crystals of the fcc CoCrFeNiAl0.3 (at %) high-entropy alloy (HEA) under tensile strain. It was shown that ageing of the CoCrFeNiAl0.3 HEA single crystals at a temperature of 823 K for 150 hours and at 893 K for 50 hours, results in the precipitation of γ′-phase particles of size d < 5 nm, with L12-type ordering. In the [1̅11]-oriented crystals, precipitation of γ′-phase particles leads to an increase in critical shear stresses τcr by 25–30 MPa in the temperature range T = 77–873 K, a decrease in the strain hardening coefficient Θ = dσ/dε and an increase in plasticity of 11–14% relative to the initial crystals without particles. The decrease in Θ = dσ/dε and the increase in plasticity are associated with the influence of the γ′-phase particles on the localization of the deformation, predominantly in one system. [ABSTRACT FROM AUTHOR] |
| Databáze: |
Complementary Index |
| Externí odkaz: |
|