Journal of Materials Science: Materials in Electronics; Mar2019, Vol. 30 Issue 6, p5640-5651, 12p |
| Abstrakt: |
The effect of sintering temperature on the microstructure, density and nonlinear electrical properties of 0.1 mol% Nb2O5 added ZnO-V2O5 varistor ceramics had been investigated. Density measurement, scanning electron microscopy (SEM), X-ray diffraction (XRD) pattern analysis characterized the sintered samples. The electric current and capacitance measurements of the varistor samples were done in varying voltage over a wide range. Image analysis by SEM shows an increase in the average grain size from 2.8 to 7.2 µm when the sintering temperature increases from 850 to 975 °C. The varistor sample, sintered at 850 °C, exhibits breakdown field of 4258 V/cm with nonlinear exponent value of 24. Degradation in breakdown field (1440 V/cm) and nonlinear exponent (9) have been observed with an increase in sintering temperature up to 975 °C. Barrier height estimated from the electric field-current density (E-J) and the capacitance-voltage (C-V) measurements follow an inverse relationship with sintering temperature. [ABSTRACT FROM AUTHOR] |
| Databáze: |
Complementary Index |
| Externí odkaz: |
|
Full text from SpringerLink