| Abstrakt: |
Titania nanostructures were synthesized by hydrothermal method. Titanium tetrachloride was used as a precursor, sodium hydroxide was used as a solvent. Effect on their morphology by variation of parameters like temperature (110°C, 160°C and 180°C), time (15h,18h, 20h, 22h, 24h) and concentration of the solvent NaOH (5M, 8M, 10 M, 12M) were studied. The obtained TiO2 nanostructures were washed with deionized water. The structure, size, morphology of the prepared nanostructures were analyzed by SEM (scanning electron microscope), DLS (dynamic light scattering), TEM (transmission electron microscope). SEM and TEM revealed the shape, size of the nanostructures. DLS reported the particle size of prepared TiO2 nanoparticles. Polymeric films based on polyvinyl alcohol (PVA) doped with titanium dioxide nanostructures at different weight percentage (0.5, 0.75, 1,2 TiO2/PVA) were prepared using the ultra sonication and solution casting techniques. The appropriate weight of PVA was dissolved in deionized water. The mixture was magnetically stirred continuously and heated (80°C) for 4 hours, until the solution mixture becomes homogenous. Different weight percentage of TiO2 nanostructures were added to deionized water and sonicated for 3 hours to prevent the nanostructures agglomeration. The mixture was mixed with the PVA solution and magnetically stirred for 1 hour to get good dispersion without agglomeration. The final PVA /TiO2 mixture were casted in glass Petridish, were left until dry. Ultrasonication was used as a major factor for preparation in order to get better dispersion. Nanocomposite films were characterized using SEM and were found to exhibit antimicrobial properties when treated with E.coli and pseudomonas. [ABSTRACT FROM AUTHOR] |