Castaing, Victor, Sontakke, Atul D., Fernández‐Carrión, Alberto José, Touati, Nadia, Binet, Laurent, Allix, Mathieu, Gourier, Didier, Viana, Bruno |
| Předmět: |
|
| Zdroj: |
European Journal of Inorganic Chemistry; 12/1/2017, Vol. 2017 Issue 44, p5114-5120, 7p |
| Abstrakt: |
Highly transparent glass ceramics, synthesized from a glass precursor with a nominal composition of SiO2/ZnO/Ga2O3/Na2O/Cr2O3 (65:17:23:5:0.125), were prepared by glass crystallization. This method enables the synthesis of up to 50 wt.-% of size-controllable Cr3+-doped ZnGa2O4 nanocrystals embedded in an SiO2-rich glass matrix after crystallization at 900-1000 °C for 10 min. Rietveld refinements and transmission electron microscopy imaging showed that the nanoparticle sizes are ca. 16 and 33 nm for the glass ceramics annealed at 900 and 1000 °C, respectively. Photoluminescence measurements of these glass ceramics revealed intense deep red ( λ = 695 nm) persistent emission that is detectable for up to 10 h, similar to that previously observed for ZnGa2O4 powder. As the glass ceramics exhibit good transparency, the persistent glow arises from the entire sample volume, which is of interest for outdoor applications and for more detailed studies of the mechanism for the persistent luminescence. Thermoluminescence measurements showed a wide distribution of trap depths centered at ca. 325 K. The traps can be charged not only under UV light but also under visible-light excitation from λ = 365 to 625 nm. Electron paramagnetic resonance spectroscopy measurements of the Cr3+ ions showed clearly that the ZnGa2O4 nanocrystals in the glass ceramics exhibit the same types of defects and disorder as those in microcrystalline ZnGa2O4 powder, and this suggests that antisite defects are the dominant traps responsible for the persistent luminescence. It is proposed that the ability to charge ZnGa2O4 particles with visible light can be attributed to the combination of a two-photon absorption and a local electric field owing to antisite defects in the vicinities of some of the Cr3+ ions. [ABSTRACT FROM AUTHOR] |
| Databáze: |
Complementary Index |
| Externí odkaz: |
|