| Autor: |
Choi, Hyeongdo, Kim, Sun Jin, Kim, Yongjun, We, Ju Hyung, Oh, Min-Wook, Cho, Byung Jin |
| Zdroj: |
Journal of Materials Chemistry C; 9/7/2017, Vol. 5 Issue 33, p8559-8565, 7p |
| Abstrakt: |
A cost-effective and large-scale thermoelectric (TE) energy harvester is becoming increasingly important for energy recovery systems such as self-powered electronics and renewable power generation. Here, we report on a TE device composed of p-type Bi0.5Sb1.5Te3 and n-type Bi2Te2.7Se0.3 TE materials prepared using a screen-printing process, which has the advantages of low cost, scalability to large areas and the ability to form a flexible TE generator. The TE properties of the screen-printed TE thick films were optimized via subsequent annealing with mechanical pressure. It was found that thermal annealing with the application of mechanical pressure plays a key role in controlling the carrier concentration and improving the density of the TE thick films. Under optimized annealing conditions, the Bi0.5Sb1.5Te3 (p-type) thick film had a ZT of 0.89 and a density of 5.67 g cm−3 while the Bi2Te2.7Se0.3 (n-type) thick film had a ZT of 0.57 and a density of 5.68 g cm−3 at room temperature. TE generators composed of 72 and 200 couples were fabricated with these thick films. The output power of the device composed of 72 couples was 0.1 W for a temperature difference (ΔT) of 28 K. Another device with 200 couples generated 0.31 W of electric power for the same ΔT. [ABSTRACT FROM AUTHOR] |
| Databáze: |
Complementary Index |
| Externí odkaz: |
|