Surface Review & Letters; Oct2017, Vol. 24 Issue 7, p-1, 8p |
| Abstrakt: |
The NiO/YSZ anode materials of SOFCs with Bi2O3 as sintering aids were successfully prepared by dry-pressing process. The effects of Bi2O3 content on the sintering properties of NiO/YSZ anode materials were studied, including the effects on the density, open porosity, weight loss, phase composition, microstructure, mechanical strength and electrical conductivity. In particular, the weight loss, relative density and bending strength of the sintered NiO/YSZ ceramics increased with the increase of Bi2O3 content while the open porosity decreased gradually. The density of the NiO-YSZ ceramics with 6wt.% Bi2O3 sintered at 1250C could reach that of the ceramics without Bi2O3 sintered at 1400C. For Bi2O3 concentration higher than 6wt.%, phase transformation of zirconia from monoclinic to cubic structure occurs, causing volume change and microcracks in the anode materials. Therefore, the optimum adding amount of Bi2O3 is 6wt.%, which can reduce the sintering temperature to 1250C. The ceramics with 6wt.% Bi2O3 have relatively high bending strength and low sintering temperature. This is of great significance for improving the performance of the anode and cutting the cost. [ABSTRACT FROM AUTHOR] |
| Databáze: |
Complementary Index |
| Externí odkaz: |
|