Tadge, Prashant, Sasikumar, C. |
| Předmět: |
|
| Zdroj: |
AIP Conference Proceedings; 2016, Vol. 1728 Issue 1, p020294-1-020294-4, 4p, 2 Charts, 3 Graphs |
| Abstrakt: |
In recent days surface mechanical attrition treatment (SMAT) had attracted the attention of researchers as it produces a nano-crystalline surface with improved mechanical properties. In the present study Al-4%Cu alloy used in automobile and aerospace application is subjected to surface mechanical attrition treatment using steel shots. The microstructural changes introduced on the surface of the Al alloy was investigated using Scanning Electron Microscopy (SEM). The secondary phases formed during the SMAT process is been investigated using EDX and XRD analysis. The effects of SMAT on the mechanical properties were analyzed using a tensile testing. The SMA treatment had resulted in severe plastic deformation of the surface, thereby yielded a nanocrystalline surface with a grain size of 30 to 50 nm. Further, it is alsofound that the SMAT produced ultra nanocrystalline particles of Cu2Al dispersed uniformly into α-Al matrix. These microstructural changes had resulted in considerable change in the mechanical properties of these alloys. The tensile strength of these alloys had increased from ∼212 MPa to 303 MPa while the fracture toughness increased up to 28% in 10 minutes of SMAT. [ABSTRACT FROM AUTHOR] |
| Databáze: |
Complementary Index |
| Externí odkaz: |
|