| Autor: |
Radoman, T. S., Džunuzović, J. V., Trifković, K. T., Palija, T., Marinković, A. D., Bugarski, B., Dſunuzović, E. S. |
| Předmět: |
|
| Zdroj: |
Express Polymer Letters; 2015, Vol. 9 Issue 10, p916-931, 16p, 2 Color Photographs, 1 Black and White Photograph, 1 Diagram, 4 Charts, 8 Graphs |
| Abstrakt: |
Novel soy alkyd-based nanocomposites (NCs) were prepared using TiO2 nanoparticles (NPs) surface modified with different gallates, and for the first time with imine obtained from 3,4-dihydroxybenzaldehyde and oleylamine (DHBAOA). Unmodified and surface modified anatase TiO2 NPs were characterized by transmission electron microscopy (TEM), X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR) and ultraviolet-visible (UV-Vis) spectroscopy, while the amount of adsorbed ligands was calculated from thermogravimetric analysis (TGA) results. Surface modification of TiO2 NPs was confirmed by FTIR and UV-Vis spectra. The influence of the TiO2 surface modification on the dispersion of TiO2 NPs in alkyd resin, thermal, barrier and mechanical properties and chemical resistance of alkyd resin/ TiO2 NC coatings was investigated. The obtained results revealed that glass transition temperature of all investigated NCs is lower than for pure resin, that the presence of TiO2 NPs surface modified with gallates had no significant influence on the thermooxidative stability of alkyd resin, while TiO2-DHBAOA NPs slightly improved alkyd resin thermooxidative stability. Also, the presence of surface modified TiO2 NPs improved barrier properties, increased stress and strain at break and hardness and chemical resistance and decreased modulus of elasticity and abrasion resistance of alkyd resin. [ABSTRACT FROM AUTHOR] |
| Databáze: |
Complementary Index |
| Externí odkaz: |
|