Transition metal vacancy and position engineering enables reversible anionic redox reaction for sodium storage.

Autor: Cai C; State Key Laboratory of Advanced Technology for Materials Synthesis and Processing, Wuhan University of Technology, Wuhan, 430070, China., Li X; State Key Laboratory of Advanced Technology for Materials Synthesis and Processing, Wuhan University of Technology, Wuhan, 430070, China., Li J; Chemical Sciences and Engineering Division, Argonne National Laboratory, Lemont, IL, 60439, USA. jiantao_work@126.com., Yu R; State Key Laboratory of Advanced Technology for Materials Synthesis and Processing, Wuhan University of Technology, Wuhan, 430070, China., Hu P; State Key Laboratory of Advanced Technology for Materials Synthesis and Processing, Wuhan University of Technology, Wuhan, 430070, China., Zhu T; State Key Laboratory of Advanced Technology for Materials Synthesis and Processing, Wuhan University of Technology, Wuhan, 430070, China., Li T; X-ray Science Division, Advanced Photon Source, Argonne National Laboratory, Lemont, IL, 60439, USA., Lee S; X-ray Science Division, Advanced Photon Source, Argonne National Laboratory, Lemont, IL, 60439, USA., Xu N; State Key Laboratory of Advanced Technology for Materials Synthesis and Processing, Wuhan University of Technology, Wuhan, 430070, China., Fan H; State Key Laboratory of Advanced Technology for Materials Synthesis and Processing, Wuhan University of Technology, Wuhan, 430070, China., Wu J; State Key Laboratory of Advanced Technology for Materials Synthesis and Processing, Wuhan University of Technology, Wuhan, 430070, China., Zhou L; State Key Laboratory of Advanced Technology for Materials Synthesis and Processing, Wuhan University of Technology, Wuhan, 430070, China. liangzhou@whut.edu.cn., Mai L; State Key Laboratory of Advanced Technology for Materials Synthesis and Processing, Wuhan University of Technology, Wuhan, 430070, China. mlq518@whut.edu.cn., Amine K; Chemical Sciences and Engineering Division, Argonne National Laboratory, Lemont, IL, 60439, USA. amine@anl.gov.; Pritzker School of Molecular Engineering, The University of Chicago, Chicago, IL, 60637, USA. amine@anl.gov.
Jazyk: angličtina
Zdroj: Nature communications [Nat Commun] 2025 Jan 02; Vol. 16 (1), pp. 100. Date of Electronic Publication: 2025 Jan 02.
DOI: 10.1038/s41467-024-54998-1
Abstrakt: Triggering the anionic redox reaction is an effective approach to boost the capacity of layered transition metal (TM) oxides. However, the irreversible oxygen release and structural deterioration at high voltage remain conundrums. Herein, a strategy for Mg ion and vacancy dual doping with partial TM ions pinned in the Na layers is developed to improve both the reversibility of anionic redox reaction and structural stability of layered oxides. Both the Mg ions and vacancies (□) are contained in the TM layers, while partial Mn ions (~1.1%) occupy the Na-sites. The introduced Mg ions combined with vacancies not only create abundant nonbonding O 2p orbitals in favor of high oxygen redox capacity, but also suppress the voltage decay originated from Na-O-□ configuration. The Mn ions pinned in the Na layers act as "rivets" to restrain the slab gliding at extreme de-sodiated state and thereby inhibit the generation of cracks. The positive electrode, Na 0.67 Mn 0.011 [Mg 0.1 □ 0.07 Mn 0.83 ]O 2 , delivers an enhanced discharge capacity and decent cyclability. This study provides insights into the construction of stable layered oxide positive electrode with highly reversible anionic redox reaction for sodium storage.
Competing Interests: Competing interests: The authors declare no competing interests.
(© 2024. The Author(s).)
Databáze: MEDLINE
Externí odkaz: