High-Performance Dental Resins Containing a Starburst Monomer.

Autor:	Dai SQ; State Key Laboratory of Oral & Maxillofacial Reconstruction and Regeneration, National Clinical Research Center for Oral Diseases, Shaanxi Key Laboratory of Stomatology, Department of Prosthodontics, School of Stomatology, The Fourth Military Medical University, Xi'an, China., Zhou W; State Key Laboratory of Oral & Maxillofacial Reconstruction and Regeneration, National Clinical Research Center for Oral Diseases, Shaanxi Key Laboratory of Stomatology, Department of Prosthodontics, School of Stomatology, The Fourth Military Medical University, Xi'an, China., Duan LY; State Key Laboratory of Oral & Maxillofacial Reconstruction and Regeneration, National Clinical Research Center for Oral Diseases, Shaanxi Key Laboratory of Stomatology, Department of Prosthodontics, School of Stomatology, The Fourth Military Medical University, Xi'an, China., Tang K; State Key Laboratory of Oral & Maxillofacial Reconstruction and Regeneration, National Clinical Research Center for Oral Diseases, Shaanxi Key Laboratory of Stomatology, Department of Prosthodontics, School of Stomatology, The Fourth Military Medical University, Xi'an, China., Yang ZY; State Key Laboratory of Oral & Maxillofacial Reconstruction and Regeneration, National Clinical Research Center for Oral Diseases, Shaanxi Key Laboratory of Stomatology, Department of Prosthodontics, School of Stomatology, The Fourth Military Medical University, Xi'an, China.; Department of Stomatology, 923th Hospital of the Joint Logistics Support Force of PLA, Nanning, China., Cao RJ; State Key Laboratory of Oral & Maxillofacial Reconstruction and Regeneration, National Clinical Research Center for Oral Diseases, Shaanxi Key Laboratory of Stomatology, Department of Prosthodontics, School of Stomatology, The Fourth Military Medical University, Xi'an, China., Tay FR; The Dental College of Georgia, Augusta University, Augusta, GA, USA., Niu LN; State Key Laboratory of Oral & Maxillofacial Reconstruction and Regeneration, National Clinical Research Center for Oral Diseases, Shaanxi Key Laboratory of Stomatology, Department of Prosthodontics, School of Stomatology, The Fourth Military Medical University, Xi'an, China., Chen JH; State Key Laboratory of Oral & Maxillofacial Reconstruction and Regeneration, National Clinical Research Center for Oral Diseases, Shaanxi Key Laboratory of Stomatology, Department of Prosthodontics, School of Stomatology, The Fourth Military Medical University, Xi'an, China.
Jazyk:	angličtina
Zdroj:	Journal of dental research [J Dent Res] 2024 May; Vol. 103 (5), pp. 536-545. Date of Electronic Publication: 2024 Mar 28.
DOI:	10.1177/00220345241232312
Abstrakt:	Dimethacrylate-based chemistries feature extensively as resin monomers in dental resin-based materials due to their distinguished overall performance. However, challenges endure, encompassing inadequate mechanical attributes, volumetric shrinkage, and estrogenicity. Herein, we first synthesized a novel resin monomer, 9-armed starburst polyurethane acrylate (NPUA), via the grafting-onto approach. Compared to the primary commercial dental monomer 2,2-bis [p-(2'-hydroxy-3'-methacryloxypropoxy) phenyl] propane (Bis-GMA) (with a viscosity of 1,174 ± 3 Pa·s and volumetric shrinkage of 4.7% ± 0.1%), the NPUA monomer achieves the lower viscosity (158 ± 1 Pa·s), volumetric shrinkage (2.5% ± 0.1%), and cytotoxicity ( P < 0.05). The NPUA-based resins exhibit the higher flexural strength, flexural modulus, hardness, and hydrophobicity and lower volumetric shrinkage, water absorption, and solubility compared to the Bis-GMA (70 wt%)/TEGDMA (30 wt%) resins. The NPUA-based composites exhibit significantly higher flexural strength, flexural modulus, and hardness and lower volumetric shrinkage (171.4 ± 3.0 MPa, 12.6 ± 0.5 GPa, 2.0 ± 0.2 GPa, and 3.4% ± 0.2%, respectively) compared to the Bis-GMA group (120.3 ± 4.7 MPa, 9.4 ± 0.7 GPa, 1.5 ± 0.1 GPa, and 4.7% ± 0.2%, respectively; P < 0.05). This work presents a viable avenue for augmenting the physicochemical attributes of dental resins. Competing Interests: Declaration of Conflicting InterestsThe authors declared no potential conflicts of interest with respect to the research, authorship, and/or publication of this article.
Databáze:	MEDLINE
Externí odkaz:	Zobrazit plný text záznamu