Tambe AB; Centre for Materials for Electronics Technology Off Pashan Road, Panchwati Pune-411008 Maharashtra India sudhir1305@gmail.com bbkale1@gmail.com., Arbuj SS; Centre for Materials for Electronics Technology Off Pashan Road, Panchwati Pune-411008 Maharashtra India sudhir1305@gmail.com bbkale1@gmail.com., Umarji GG; Centre for Materials for Electronics Technology Off Pashan Road, Panchwati Pune-411008 Maharashtra India sudhir1305@gmail.com bbkale1@gmail.com., Kulkarni SK; Centre for Materials for Electronics Technology Off Pashan Road, Panchwati Pune-411008 Maharashtra India sudhir1305@gmail.com bbkale1@gmail.com., Kale BB; Centre for Materials for Electronics Technology Off Pashan Road, Panchwati Pune-411008 Maharashtra India sudhir1305@gmail.com bbkale1@gmail.com.; MIT World Peace University (MIT-WPU) Paud Rd, Kothrud Pune Maharashtra 411038 India. |
| Jazyk: |
angličtina |
| Zdroj: |
RSC advances [RSC Adv] 2023 Dec 04; Vol. 13 (50), pp. 35369-35378. Date of Electronic Publication: 2023 Dec 04 (Print Publication: 2023). |
| DOI: |
10.1039/d3ra07321a |
| Abstrakt: |
Herein, we demonstrated the in situ synthesis of g-C 3 N 4 /Ti 3 C 2 T x nano-heterostructures for hydrogen generation under UV visible light irradiation. The formation of the g-C 3 N 4 /Ti 3 C 2 T x nano-heterostructures was confirmed via powder X-ray diffraction and supported by XPS. The FE-SEM images indicated the formation of layered structures of MXene and g-C 3 N 4 . HR-TEM images and SAED patterns confirmed the presence of g-C 3 N 4 together with Ti 3 C 2 T x nanosheets, i.e. , the formation of nano-heterostructures of g-C 3 N 4 /Ti 3 C 2 T x . The absorption spectra clearly showed the distinct band gaps of g-C 3 N 4 and Ti 3 C 2 T x in the nano-heterostructure. The increase in PL intensity and broadening of the peak with an increase in g-C 3 N 4 indicated the suppression of electron-hole recombination. Furthermore, the nano-heterostructure was used as a photocatalyst for H 2 generation from water and methylene blue dye degradation. The highest H 2 evolution (1912.25 μmol/0.1 g) with good apparent quantum yield (3.1%) and an efficient degradation of MB were obtained for gCT-0.75, which was much higher compared to that of the pristine materials. The gCT-0.75 nano-heterostructure possessed a high surface area and abundant vacancy defects, facilitating the separation of charge carriers, which was ultimately responsible for this high photocatalytic activity. Additionally, TRPL clearly showed a higher decay time, which supports the enhancement in the photocatalytic activity of the gCT-0.75 nano-heterostructure. The nano-heterostructure with the optimum concentration of g-C 3 N 4 formed a hetero-junction with the linked catalytic system, which facilitated efficient charge carrier separation also responsible for the enhanced photocatalytic activity.
Competing Interests: There are no conflicts to declare.
(This journal is © The Royal Society of Chemistry.) |
| Databáze: |
MEDLINE |
| Externí odkaz: |
|