| Autor: |
Abdul Razak NI; Faculty of Chemical and Energy Engineering, Universiti Teknologi Malaysia, Johor Bahru 81310, Johor, Malaysia., Yusoff NISM; Advanced Membrane Technology Research Centre (AMTEC), Universiti Teknologi Malaysia, Johor Bahru 81310, Johor, Malaysia., Ahmad MH; Institute of High Voltage and High Current, School of Electrical Engineering, Universiti Teknologi Malaysia, Johor Bahru 81310, Johor, Malaysia., Zulkifli M; Green Chemistry and Sustainability Cluster, Branch Campus, Malaysian Institute of Chemical and Bioengineering Technology, Universiti Kuala Lumpur, Taboh Naning, Alor Gajah 78000, Melaka, Malaysia., Wahit MU; Faculty of Chemical and Energy Engineering, Universiti Teknologi Malaysia, Johor Bahru 81310, Johor, Malaysia.; Centre for Advanced Composite Materials (CACM), Universiti Teknologi Malaysia, Johor Bahru 81310, Johor, Malaysia. |
| Abstrakt: |
Crosslinked polyethylene (XLPE) nanocomposite has superior insulation performance due to its excellent dielectric, mechanical, and thermal properties. The incorporation of nano-sized fillers drastically improved these properties in XLPE matrix due to the reinforcing effect of interfacial region between the XLPE-nanofillers. Good interfacial strength can be further improved by introducing a hybrid system nanofiller as a result of synergistic interaction between the nanofiller relative to a single filler system. Another factor affecting interfacial strength is the amount of hybrid nanofiller. Therefore, the incorporation amount of hybridising layered double hydroxide (LDH) with aluminium oxide (Al 2 O 3 ) nanofiller into the XLPE matrix was investigated. Herein, the influence of hybrid nanofiller content and the 1:1 ratio of LDH to Al 2 O 3 on the dielectric, mechanical, and thermal properties of the nanocomposite was studied. The structure and morphology of the XLPE/LDH-Al 2 O 3 nanocomposites revealed that the hybridisation of nanofiller improved the dispersion state. The dielectric, mechanical, and thermal properties, including partial discharge resistance, AC breakdown strength, and tensile properties (tensile strength, Young's modulus, and elongation at break) were enhanced since it was influenced by the synergetic effect of the LDH-Al 2 O 3 nanofiller . These properties were increased at optimal value of 0.8 wt.% before decreasing with increasing hybrid nanofiller. It was found that the value of PD magnitude improvement went down to 47.8% and AC breakdown strength increased by 15.6% as compared to pure XLPE. The mechanical properties were enhanced by 14.4%, 31.7%, and 23% for tensile strength, Young's modulus, and elongation at break, respectively. Of note, the hybridisation of nanofillers opens a new perspective in developing insulating material based on XLPE nanocomposite. |