Effects of in vitro erosion on surface texture, microhardness, and color stability of resin composite with S-PRG fillers.

Autor: Pimentel ES; Faculdade São Leopoldo Mandic, Instituto de Pesquisas São Leopoldo Mandic, Rua José Rocha Junqueira, 13, Campinas, SP, CEP, 13045-755, Brazil., França FMG; Faculdade São Leopoldo Mandic, Instituto de Pesquisas São Leopoldo Mandic, Rua José Rocha Junqueira, 13, Campinas, SP, CEP, 13045-755, Brazil., Turssi CP; Faculdade São Leopoldo Mandic, Instituto de Pesquisas São Leopoldo Mandic, Rua José Rocha Junqueira, 13, Campinas, SP, CEP, 13045-755, Brazil., Basting RT; Faculdade São Leopoldo Mandic, Instituto de Pesquisas São Leopoldo Mandic, Rua José Rocha Junqueira, 13, Campinas, SP, CEP, 13045-755, Brazil., Vieira-Junior WF; Faculdade São Leopoldo Mandic, Instituto de Pesquisas São Leopoldo Mandic, Rua José Rocha Junqueira, 13, Campinas, SP, CEP, 13045-755, Brazil. waldemir.f@hotmail.com.
Jazyk: angličtina
Zdroj: Clinical oral investigations [Clin Oral Investig] 2023 Jul; Vol. 27 (7), pp. 3545-3556. Date of Electronic Publication: 2023 Mar 30.
DOI: 10.1007/s00784-023-04968-6
Abstrakt: Objectives: To evaluate the effect of acid erosion on different physical properties of resin composite with S-PRG (surface pre-reacted glass) fillers, by conducting simulations of intrinsic and extrinsic sources.
Materials and Methods: Cylindrical samples (Ø6 vs. 2 mm) of a conventional nanohybrid resin composite (Forma, Ultradent) and of a nanohybrid resin composite with S-PRG filler (Beautifil II, Shofu) were exposed to erosive cycling (5 days), based on (n=12) remineralizing solution (control); 0.3% citric acid (pH=2.6); or 0.01 M hydrochloric acid (pH=2). Roughness (Ra), microhardness (KHN), and color (CIEL*a*b*, CIEDE2000, and Vita scale (SGU)) factors were analyzed at the initial and final time points, and the general color changes (ΔE ab , ΔE 00 , ΔSGU) were calculated. Final images were obtained using scanning electron microscopy (SEM). The data were evaluated by generalized models, Mann-Whitney, Wilcoxon, Kruskal-Wallis, and Dunn tests (α=0.05).
Results: Regarding KHN, there was no difference between the groups or the time periods (p = 0.74). As for Ra, there was a significant increase in the Ra of both composites after cycling with hydrochloric acid, but only the resin composite with S-PRG filler showed a change in Ra after cycling with citric acid (p = 0.003). After cycling with citric and hydrochloric acid, the highest Ra values were found for the resin composite with S-PRG filler (p < 0.0001), corroborating the result of images (SEM) indicating loss of filler and porosities in this material. The resin composite with S-PRG filler showed higher ΔE ab and ΔE 00 , in addition to more negative ΔSGU values and lower L* values after exposure to both acids, compared to the control (p < 0.05).
Conclusion: The acidic conditions altered the roughness and color stability of the materials tested, pointing out that the resin composite containing S-PRG filler showed greater degradation of its physical properties than the conventional resin composite.
Clinical Relevance: Bioactive materials are relevant, considering that their properties interact with dental hard tissues; however, the S-PRG-based resin composite showed greater degradation under acidic conditions than the conventional resin composite.