The Influence of Reactive PS-PVD Process Parameters on the Microstructure and Thermal Properties of Yb 2 Zr 2 O 7 Thermal Barrier Coating.

Autor: Pędrak P; Research and Development Laboratory for Aerospace Materials, Rzeszow University of Technology, Powstańców Warszawy 12, 35-959 Rzeszów, Poland., Góral M; Research and Development Laboratory for Aerospace Materials, Rzeszow University of Technology, Powstańców Warszawy 12, 35-959 Rzeszów, Poland., Dychton K; Research and Development Laboratory for Aerospace Materials, Rzeszow University of Technology, Powstańców Warszawy 12, 35-959 Rzeszów, Poland., Drajewicz M; Research and Development Laboratory for Aerospace Materials, Rzeszow University of Technology, Powstańców Warszawy 12, 35-959 Rzeszów, Poland., Wierzbinska M; Research and Development Laboratory for Aerospace Materials, Rzeszow University of Technology, Powstańców Warszawy 12, 35-959 Rzeszów, Poland., Kubaszek T; Research and Development Laboratory for Aerospace Materials, Rzeszow University of Technology, Powstańców Warszawy 12, 35-959 Rzeszów, Poland.
Jazyk: angličtina
Zdroj: Materials (Basel, Switzerland) [Materials (Basel)] 2022 Feb 21; Vol. 15 (4). Date of Electronic Publication: 2022 Feb 21.
DOI: 10.3390/ma15041594
Abstrakt: Ytterbium zirconate (Yb 2 Zr 2 O 7 ) is one of the most promising materials for yttria-stabilized zirconia (YSZ) replacement as a thermal barrier coating (TBCs) application. In the presented report, the experimental synthesis of Yb 2 Zr 2 O 7 coating using novel Reactive Plasma Spray Physical Vapor Deposition (Reactive PS-PVD) is described. The obtained coating, irrespective of the power current (1800, 2000 and 2200 A), was characterized by a hybrid structure and a thickness of about 80-110 μm. The results of XRD phase analysis showed the formation of ytterbium zirconate in the coating but the presence of ytterbium and zirconium oxides was also detected. The oxides were not observed in calcinated powder. The decrease in thermal conductivity with power current increase was observed. It was the result of higher thickness and better columnar structure of the coating obtained using higher power current of the plasma torch.
Databáze: MEDLINE
Nepřihlášeným uživatelům se plný text nezobrazuje