Esposito E; Institute on Membrane Technology, CNR-ITM, Via P. Bucci 17/C, 87036 Rende, Italy., Minotti A; MIPRONS srl, Via Lauri 32, 00037 Segni, Italy., Fontananova E; Institute on Membrane Technology, CNR-ITM, Via P. Bucci 17/C, 87036 Rende, Italy., Longo M; Institute on Membrane Technology, CNR-ITM, Via P. Bucci 17/C, 87036 Rende, Italy., Jansen JC; Institute on Membrane Technology, CNR-ITM, Via P. Bucci 17/C, 87036 Rende, Italy., Figoli A; Institute on Membrane Technology, CNR-ITM, Via P. Bucci 17/C, 87036 Rende, Italy. |
| Abstrakt: |
Low-temperature electrolysis by using polymer electrolyte membranes (PEM) can play an important role in hydrogen energy transition. This work presents a study on the performance of a proton exchange membrane in the water electrolysis process at room temperature and atmospheric pressure. In the perspective of applications that need a device with small volume and low weight, a miniaturized electrolysis cell with a 36 cm 2 active area of PEM over a total surface area of 76 cm 2 of the device was used. H 2 and O 2 production rates, electrical power, energy efficiency, Faradaic efficiency and polarization curves were determined for all experiments. The effects of different parameters such as clamping pressure and materials of the electrodes on polarization phenomena were studied. The PEM used was a catalyst-coated membrane (Ir-Pt-Nafion™ 117 CCM). The maximum H 2 production was about 0.02 g min -1 with a current density of 1.1 A cm -2 and a current power about 280 W. Clamping pressure and the type of electrode materials strongly influence the activation and ohmic polarization phenomena. High clamping pressure and electrodes in titanium compared to carbon electrodes improve the cell performance, and this results in lower ohmic and activation resistances. |