Development of a sample preparation procedure for Sr isotope analysis of Portland cements.

Autor: Kazlagić A; Division 1.1 Inorganic Trace Analysis, Federal Institute for Materials Research and Testing, Richard-Willstäter-Straße 11, 12489, Berlin, Germany. anera.kazlagic@bam.de., Russo FF; Division 1.1 Inorganic Trace Analysis, Federal Institute for Materials Research and Testing, Richard-Willstäter-Straße 11, 12489, Berlin, Germany., Vogl J; Division 1.1 Inorganic Trace Analysis, Federal Institute for Materials Research and Testing, Richard-Willstäter-Straße 11, 12489, Berlin, Germany., Sturm P; Division 7.4 Technology of Construction Materials, Federal Institute for Materials Research and Testing, Unter den Eichen 87, 12205, Berlin, Germany., Stephan D; Department of Civil Engineering, Building Materials and Construction Chemistry, Technische Universität Berlin, Gustav-Meyer-Allee 25, 13355, Berlin, Germany., Gluth GJG; Division 7.4 Technology of Construction Materials, Federal Institute for Materials Research and Testing, Unter den Eichen 87, 12205, Berlin, Germany.
Jazyk: angličtina
Zdroj: Analytical and bioanalytical chemistry [Anal Bioanal Chem] 2022 Jun; Vol. 414 (15), pp. 4379-4389. Date of Electronic Publication: 2022 Jan 14.
DOI: 10.1007/s00216-021-03821-7
Abstrakt: The 87 Sr/ 86 Sr isotope ratio can, in principle, be used for provenancing of cement. However, while commercial cements consist of multiple components, no detailed investigation into their individual 87 Sr/ 86 Sr isotope ratios or their influence on the integral 87 Sr/ 86 Sr isotope ratio of the resulting cement was conducted previously. Therefore, the present study aimed at determining and comparing the conventional 87 Sr/ 86 Sr isotope ratios of a diverse set of Portland cements and their corresponding Portland clinkers, the major component of these cements. Two approaches to remove the additives from the cements, i.e. to measure the conventional 87 Sr/ 86 Sr isotopic fingerprint of the clinker only, were tested, namely, treatment with a potassium hydroxide/sucrose solution and sieving on a 11-µm sieve. Dissolution in concentrated hydrochloric acid/nitric acid and in diluted nitric acid was employed to determine the 87 Sr/ 86 Sr isotope ratios of the cements and the individual clinkers. The aim was to find the most appropriate sample preparation procedure for cement provenancing, and the selection was realised by comparing the 87 Sr/ 86 Sr isotope ratios of differently treated cements with those of the corresponding clinkers. None of the methods to separate the clinkers from the cements proved to be satisfactory. However, it was found that the 87 Sr/ 86 Sr isotope ratios of clinker and cement generally corresponded, meaning that the latter can be used as a proxy for the clinker 87 Sr/ 86 Sr isotope ratio. Finally, the concentrated hydrochloric acid/nitric acid dissolution method was found to be the most suitable sample preparation method for the cements; it is thus recommended for 87 Sr/ 86 Sr isotope analyses for cement provenancing.
(© 2022. The Author(s).)