The Effect of the Synthetic Procedure of Acrylonitrile-Acrylic Acid Copolymers on Rheological Properties of Solutions and Features of Fiber Spinning.

Autor: Skvortsov IY; A.V. Topchiev Institute of Petrochemical Synthesis, Russian Academy of Sciences, Leninsky Av., 29, 119991 Moscow, Russia., Chernikova EV; A.V. Topchiev Institute of Petrochemical Synthesis, Russian Academy of Sciences, Leninsky Av., 29, 119991 Moscow, Russia.; Department of Chemistry, M.V. Lomonosov Moscow State University, Leninskiye Gory, 119991 Moscow, Russia., Kulichikhin VG; A.V. Topchiev Institute of Petrochemical Synthesis, Russian Academy of Sciences, Leninsky Av., 29, 119991 Moscow, Russia., Varfolomeeva LA; A.V. Topchiev Institute of Petrochemical Synthesis, Russian Academy of Sciences, Leninsky Av., 29, 119991 Moscow, Russia., Kuzin MS; A.V. Topchiev Institute of Petrochemical Synthesis, Russian Academy of Sciences, Leninsky Av., 29, 119991 Moscow, Russia., Toms RV; M.V. Lomonosov Institute of Fine Chemical Technologies, Russian Technological University, Vernadsky Av., 86, 119991 Moscow, Russia., Prokopov NI; M.V. Lomonosov Institute of Fine Chemical Technologies, Russian Technological University, Vernadsky Av., 86, 119991 Moscow, Russia.
Jazyk: angličtina
Zdroj: Materials (Basel, Switzerland) [Materials (Basel)] 2020 Aug 05; Vol. 13 (16). Date of Electronic Publication: 2020 Aug 05.
DOI: 10.3390/ma13163454
Abstrakt: The influence of introducing acrylic acid (AA) into the reaction mixture with acrylonitrile at the synthesis of copolymers by free-radical polymerization (FRP) and radical polymerization with reversible addition-fragmentation chain transfer (RAFT) on the rheological properties of their solutions in dimethyl sulfoxide, as well as on the capability to spin fibers by the mechanotropic method, is analyzed. The influence of AA dosing conditions on the rheological properties of the solutions in the concentration range above the crossover point was not revealed. In the case of RAFT synthesis, the rheological properties differ distinctively in the high concentration region that is expressed by unusual viscoelastic characteristics. Dilute solution viscometry revealed the influence of the comonomer loading order on the interaction intensity of the copolymer macromolecules with a solvent, which is more pronounced for samples synthesized by FRP and can be associated with the copolymers' molecular structure. Fiber spinning from solutions of polyacrylonitrile and its copolymers (PAN) synthesized by the RAFT method was not able to achieve a high degree of orientation drawing, while for polymers with a wider molecular weight distribution synthesized by FRP, it was possible to realize large stretches, which led to high-quality fibers with strength values up to 640 MPa and elongation at a break of 20%.
Databáze: MEDLINE
Nepřihlášeným uživatelům se plný text nezobrazuje