| Autor: |
Ruiz-Cañas MC; Grupo de Investigación en Química Estructural, Parque Tecnológico Guatiguará, Universidad Industrial de Santander, A.A. 678, Piedecuesta 681011, Colombia., Corredor LM; Instituto Colombiano del Petróleo, ECOPETROL S.A., A.A. 4185, Piedecuesta 681017, Colombia., Quintero HI; Instituto Colombiano del Petróleo, ECOPETROL S.A., A.A. 4185, Piedecuesta 681017, Colombia., Manrique E; Instituto Colombiano del Petróleo, ECOPETROL S.A., A.A. 4185, Piedecuesta 681017, Colombia., Romero Bohórquez AR; Grupo de Investigación en Química Estructural, Parque Tecnológico Guatiguará, Universidad Industrial de Santander, A.A. 678, Piedecuesta 681011, Colombia. |
| Jazyk: |
angličtina |
| Zdroj: |
Molecules (Basel, Switzerland) [Molecules] 2020 Jun 22; Vol. 25 (12). Date of Electronic Publication: 2020 Jun 22. |
| DOI: |
10.3390/molecules25122868 |
| Abstrakt: |
In industry, silica nanoparticles (NPs) are obtained by the fuming and the precipitation method. Fumed silica NPs are commonly used in the preparation of nanocomposites because they have an extremely low bulk density (160-190 kg/m 3 ), large surface area (50-600 m 2 /g), and nonporous surface, which promotes strong physical contact between the NPs and the organic phase. Fumed silica has fewer silanol groups (Si-OH) on its surface than the silica prepared by the Stöber method. However, the number of -OH groups on the fumed silica surface can be increased by pretreating them with sodium hydroxide (NaOH) before further surface modification. In this study, the effectiveness of the NaOH pretreatment was evaluated on commercial fumed silica NPs with a surface area of 200 m 2 /g. The number of surface -OH groups was estimated by potentiometric titration. The pretreated fumed NPs, and the precipitated NPs (prepared by the Stöber method) were modified with 3-aminopropyltriethoxysilane (APTES) to obtain A200S and nSiO 2 -APTES, respectively. The NPs were characterized using electron dispersive scanning (EDS), scanning electron microscopy (SEM), dynamic light scattering (DLS), Fourier transform infrared spectroscopy (FT-IR), thermogravimetric analysis (TGA), X-ray diffraction (XRD), BET (Brunauer-Emmett-Teller) analysis, and ζ-potential. XRD confirmed the presence of the organo-functional group on the surface of both NPs. After the amino-functionalization, the ζ-potential values of the nSiO 2 and A200 changed from -35.5 mV and -14.4 mV to +26.2 mV and +11.76 mV, respectively. Consequently, we have successfully synthesized functionalized NPs with interesting, specific surface area and porosity (pore volume and size), which can be attractive materials for chemical and energy industries. |
| Databáze: |
MEDLINE |
| Externí odkaz: |
|
|
Nepřihlášeným uživatelům se plný text nezobrazuje |
K zobrazení výsledku je třeba se přihlásit.
|