Hydrogen Evolution Reaction by Atomic Layer-Deposited MoN x on Porous Carbon Substrates: The Effects of Porosity and Annealing on Catalyst Activity and Stability.

Autor: Ramesh R; School of Materials Science and Engineering, Yeungnam University, Gyeongsan, Gyeongbuk, 38541, Republic of Korea., Sawant SY; School of Chemical Engineering, Yeungnam University, Gyeongsan, Gyeongbuk, 38541, Republic of Korea., Nandi DK; School of Materials Science and Engineering, Yeungnam University, Gyeongsan, Gyeongbuk, 38541, Republic of Korea., Kim TH; School of Materials Science and Engineering, Yeungnam University, Gyeongsan, Gyeongbuk, 38541, Republic of Korea., Kim DH; School of Materials Science and Engineering, Yeungnam University, Gyeongsan, Gyeongbuk, 38541, Republic of Korea., Han SM; School of Materials Science and Engineering, Yeungnam University, Gyeongsan, Gyeongbuk, 38541, Republic of Korea., Jang Y; Korea Basic Science Institute (KBSI), Busan Center, Busan Metropolitan City, Jinsa-dong, Gangseo-gu, 46742, Republic of Korea., Ha MG; Korea Basic Science Institute (KBSI), Busan Center, Busan Metropolitan City, Jinsa-dong, Gangseo-gu, 46742, Republic of Korea., Cho MH; School of Chemical Engineering, Yeungnam University, Gyeongsan, Gyeongbuk, 38541, Republic of Korea., Yoon T; School of Chemical Engineering, Yeungnam University, Gyeongsan, Gyeongbuk, 38541, Republic of Korea., Kim SH; School of Materials Science and Engineering, Yeungnam University, Gyeongsan, Gyeongbuk, 38541, Republic of Korea.
Jazyk: angličtina
Zdroj: ChemSusChem [ChemSusChem] 2020 Aug 21; Vol. 13 (16), pp. 4159-4168. Date of Electronic Publication: 2020 May 11.
DOI: 10.1002/cssc.202000350
Abstrakt: Molybdenum-based compounds are considered as a potential replacement for expensive precious-metal electrocatalysts for the hydrogen evolution reaction (HER) in acid electrolytes. However, coating of thin films of molybdenum nitride or carbide on a large-area self-standing substrate with high precision is still challenging. Here, MoN x is uniformly coated on carbon cloth (CC) and nitrogen-doped carbon (NC)-modified CC (NCCC) substrates by atomic layer deposition (ALD). The as-deposited film has a nanocrystalline character close to amorphous and a composition of approximately Mo 2 N with significant oxygen contamination, mainly at the surface. Among the as-prepared ALD-MoN x electrodes, the MoN x /NCCC has the highest HER activity (overpotential η≈236 mV to achieve 10 mA cm -2 ) owing to the high surface area and porosity of the NCCC substrate. However, the durability of the electrode is poor, owing to the poor adhesion of NC powder on CC. Annealing MoN x /NCCC in H 2 atmosphere at 400 °C improves both the activity and durability of the electrode without significant change in the phase or porosity. Annealing at an elevated temperature of 600 °C results in formation of a Mo 2 C phase that further enhances the activity (η≈196 mV to achieve 10 mA cm -2 ), although there is a huge reduction in the porosity of the electrode as a consequence of the annealing. The structure of the electrode is also systematically investigated by electrochemical impedance spectroscopy (EIS). A deviation in the conventional Warburg impedance is observed in EIS of the NCCC-based electrode and is ascribed to the change in the H + ion diffusion characteristics, owing to the geometry of the pores. The change in porous nature with annealing and the loss in porosity are reflected in the EIS of H + ion diffusion observed at high-frequency. The current work establishes a better understanding of the importance of various parameters for a highly active HER electrode and will help the development of a commercial electrode for HER using the ALD technique.
(© 2020 Wiley-VCH Verlag GmbH & Co. KGaA, Weinheim.)
Databáze: MEDLINE
Externí odkaz: